ANSI B16.9 ASTM A403 WP321 90Deg LR Elbow 3 Inch Sch40S
- FOB PriceUSD 1 - 1,900/Piece
- PortNingbo or Shanghai Port
- MOQ1 Piece
- Supply Ability1000 Pieces Per Day
- Payment TermsL/C,T/T,Western Union,MoneyGram
- PackagingSeaworthy plywood cases or pallets
- Delivery2 - 10 days
Quick Details
| Material: |
321
| Technics: |
Forged
| Type: | |
| Place of Origin: |
Zhejiang, China (Mainland)
| Head Code: |
Round
| Brand Name: |
Yaang
|
| Connection: |
Welding
| Shape: |
Equal
|
Packaging & Delivery
| Packaging Details: | Plywood case or fumigation woodern case |
|---|---|
| Delivery Detail: | 2 - 10 days |
Specifications
ANSI B16.9 ASTM A403 WP304 90Deg LR Elbow
1) Size: 3 Inch
THK: Sch40S
3) Material: 321
Pipe elbows are mainly used for connecting two pipes or tubes, allowing a change of direction.
We can provide short radius elbows and long radius elbows.
Usually, pipe elbows are made of carbon steels, alloy steels, stainless steel, and more.
China 90Deg LR Elbow Manufacturer Yaang supplies ANSI B16.9 ASTM A403 WP321 90Deg LR Elbow, 3 Inch, Sch40S.
Composition ranges for 321 grade stainless steel
Grade
|
C
|
Mn
|
Si
|
P
|
S
|
Cr
|
Mo
|
Ni
|
N
|
Other
| |
321
|
min.
max
|
-
0.08
|
2.00
|
0.75
|
0.045
|
0.030
|
17.0
19.0
|
-
|
9.0
12.0
|
0.10
|
Ti=5(C+N)
0.70
|
321H
|
min.
max
|
0.04
0.10
|
2.00
|
0.75
|
0.045
|
0.030
|
17.0
19.0
|
-
|
9.0
12.0
|
-
|
Ti=4(C+N)
0.70
|
347
|
min.
max
|
0.08
|
2.00
|
0.75
|
0.045
|
0.030
|
17.0
19.0
|
-
|
9.0
13.0
|
-
|
Nb=10(C+N)
1.0
|
Mechanical properties of 321 grade stainless steel
Tensile Strength (MPa) min
|
Yield Strength 0.2% Proof (MPa) min
|
Elongation (% in 50mm) min
|
Hardness
| ||
Rockwell B (HR B) max
|
Brinell (HB) max
| ||||
321
|
515
|
205
|
40
|
95
|
217
|
321H
|
515
|
205
|
40
|
95
|
217
|
347
|
515
|
205
|
40
|
92
|
201
|
321H also has a requirement for a grain size of ASTM No 7 or coarser.
| |||||
Physical properties of 321 grade stainless steel in the annealed condition
Grade
|
Density (kg/m3)
|
Elastic Modulus (GPa)
|
Mean Coefficient of Thermal Expansion (μm/m/°C)
|
Thermal Conductivity (W/m.K)
|
Specific Heat 0-100°C (J/kg.K)
|
Electrical Resistivity (nΩ.m)
| |||
0-100°C
|
0-315°C
|
0-538°C
|
at 100°C
|
at 500°C
| |||||
321
|
8027
|
193
|
16.6
|
17.2
|
18.6
|
16.1
|
22.2
|
500
|
720
|
Grade specifications for 321 grade stainless steel
Grade
|
UNS No
|
Old British
|
Euronorm
|
Swedish SS
|
Japanese JIS
| ||
BS
|
En
|
No
|
Name
| ||||
321
|
S32100
|
321S31
|
58B, 58C
|
1.4541
|
X6CrNiTi18-10
|
2337
|
SUS 321
|
321H
|
S32109
|
321S51
|
-
|
1.4878
|
X10CrNiTi18-10
|
-
|
SUS 321H
|
347
|
S34700
|
347S31
|
58G
|
1.4550
|
X6CrNiNb18-10
|
2338
|
SUS 347
|
These comparisons are approximate only. The list is intended as a comparison of functionally similar materials notas a schedule of contractual equivalents. If exact equivalents are needed original specifications must be consulted.
| |||||||
Possible alternative grades to 321 grade stainless steel
Grade
|
Why it might be chosen instead of 321
|
304L
|
The requirement is for resistance to intergranular corrosion, not for high temperature strength
|
3CR12
|
Only mild "high temperature" environment is present… up to about 600°C.
|
304H
|
Only mild "high temperature" environment is present… up to about 800°C.
|
310
|
The temperature of the operating environment is up to about 1100°C - too high for 321 or 321H.
|
S30815
(253MA)
|
The temperature of the operating environment is up to about 1150°C- too high for 321 or 321H.
|
|
APPLICATIONS:
1. Pipe and Tubes for petrochemical industry
2. Pharmaceutical industry
3. Food industry
4. Aviation and aerospace industry
5. Architectural decoration industry
6. Gas and Oil
If any inquiry, please feel free to contact by email sales@yaang.com
Related products:More>>
 |